Cím:Microstructure analisys and hardness properties of nicrbsi sprayed, flame- and laser remelted coatings [elektronikus dokumentum} / Molnár, András, Buza, Gábor, Balogh, András, Fazekas, Lajos
Dátum:2012
Megjegyzések:A szerzők által megadott adatok automatikusan feltöltve
Thermal spraying is already used in industry to protect mechanical parts against wear and corrosion, but results are not always satisfactory due to porosity, microstructures and maily bond strength. In this study, flame- (FS) and high velocity spraying (HVOF) spraying and in situ flame - and laser irradiation by laser processes were combined to modify structural characteristics of metallic NiCrBSi coatings. The microstructure evolution was studied with the chemical composition analysis by XRD and SEM coupled with EDS techniques. Results show that in situ flamke and laser remelting induces the growth of a dendritic structure which strongly decreases the porosity of as-sprayed coatings, without solidification cracking (one of the major defects that can occur during the solidification of metallic or composite alloys) and improves the mechanical properties of the layer.
ISBN:978-963-473-591-5
Tárgyszavak:Műszaki tudományok Gépészeti tudományok tanulmány, értekezés
Flame spraying
deposit
remelting
NiCrBSi alloys
micro hardness test
Megjelenés:18th "Building Services, Mechanical and Building Industry days" International Conference, 11-12 October 2012, Debrecen, Hungary [elektronikus dokumentum] / szerk. Kalmár Ferenc et al. - p. 1-10. [Paper Code: MAS 12-02]. -
További szerzők:Buza Gábor (mérnök) Balogh András (mérnök) Fazekas Lajos (1950-) (gépészmérnök)
Internet cím:Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Rekordok letöltése1 
Corvina könyvtári katalógus v8.2.27 © 2023 Monguz kft. Minden jog fenntartva.