Cím:Preparation and properties of langasite and YAG amorphous films / M. Popescu; F. Sava; A. Lorinczi; M. Stegarescu; S. Georgescu; I. N. Mihailescu; G. Socol; D. Stanoi; L. Daroczi; A Kokenyesi; M. Leonovici; D. Wagner
Dátum:2005
ISSN:1454-4164 1841-7132
Megjegyzések:Amorphous thin films of langasite and YAG have been prepared from crystals targets by pulsed laser deposition, at room temperature, in vacuum, on silicon wafers. Bulges of micrometer size are formed on the film surface. Larger size bulges (10-50 micrometers in diameter) are characteristic to the annealed langasite films. Annealing at high temperatures leads to the crystallization of the films. The annealed langasite films (850 degrees C) are polycrystalline and partially oriented with the plane (001) parallel to the surface of the silicon wafer. The bulges break easily in the heat treated films. Their empty structure was remarked on the electron microscope images. The YAG films annealed at 1100 degrees C shows a crystalline YAG phase depleted in Y and traces of Y2O3. An interesting feature is the presence of silver particles spread along the macrodefects (fracture lines) of the film.
Tárgyszavak:Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban
folyóiratcikk
langasite
YAG
pulsed laser deposition
amorphous
X-ray diffraction
crystallization
Megjelenés:Journal Of Optoelectronics And Advanced Materials. - 7 : 2 (2005), p. 963-966. -
További szerzők:Sava, F. Lorinczi, A. Stegarescu, M. Georgescu, S. Mihailescu, I. N. Socol, G. Stanoi, D. Daróczi Lajos (1965-) (fizikus) Kökényesi Sándor (1946-) (fizikus) Leonovici, M. Wagner, D.
Internet cím:Szerző által megadott URL
Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Rekordok letöltése1