Cím:	Behaviour of discontinuous gold films on SrTiO3 substrates under annealing / Imre Beszeda, Tamás Kocsis, Gergely Imreh, Frank Weigl, Hans-Gerd Boyen, Paul Ziemann, Dezső L. Beke
Dátum:	2006
ISSN:	0169-4332
Megjegyzések:	Morphological changes of thin, discontinuous gold films on SrTiO3 substrates, resulting from evaporation in the temperature range of 1143?1278 K, have been investigated by means of scanning electron microscopy (SEM) and atomic force microscopy (AFM). If the gold covered fractionof the surface is small, the evaporation kinetics can be related to the desorption of adatoms. Measuring the density of the gold beads and the timedependence of the effective thickness of the film as calculated from the diameter of the beads, the following parameters have been determined: thesurface diffusion length of the gold adatoms, ls?m???2:2?26:7 2:0? 10 3 exp? ?77 26kJ=mol=RT?, the mass transfer surface diffusion coefficient, D0s?m2=s???3:25?433 3:23? 1010 exp? ?560 49kJ=mol=RT?and the evaporation flux, J?m 2s 1??2:79?267 2:76? 1035 exp? ?426 46kJ=mol=RT?
Tárgyszavak:	Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban folyóiratcikk SrTiO3 Gold Surface diffusion Discontinuous film Evaporation
Megjelenés:	Applied Surface Science. - 253 : 3 (2006), p. 1160-1164. -
További szerzők:	Kocsis Tamás Imreh Gergely Weigl, Frank Boyen, Hans-Gerd Ziemann, Paul Beke Dezső László (1945-) (fizikus)
Internet cím:	Szerző által megadott URL DOI Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon: