Cím:Degradation of Ag/Si multilayers during heat treatments / K. Kapta, A. Csikb, L. Daróczi, Z. Papp, D. L. Beke, G. A. Langer, A. L. Greer, Z. H. Barber, M. Kis-Varga
Dátum:2003
ISSN:0042-207X
Megjegyzések:Microstructure changes during annealing of nano-crystalline silver and amorphous silicon multilayers (Ag/a-Si) have been studied by X-ray diffraction and transmission electron microscopy. The dc-magnetron sputtered Ag/a-Si multilayers remained stable even after annealing at 523 K for 10 h, and microstructural changes occurred only above 600K. The degradation of Ag/a-Si multilayers can be described by the increase of size of Ag grains, formation of grooves and pinholes at Ag grain boundaries and by the diffusion of silicon atoms through the silver grain boundaries and along the Ag/a-Si interfaces. This results in thinning of a-Si layers, and in formation of Ag granulates after longer annealing times.
Tárgyszavak:Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban
Megjelenés:Vacuum 72 : 1 (2003), p. 85-89. -
További szerzők:Csik Attila (1975-) (fizikus) Daróczi Lajos (1965-) (fizikus) Papp Zoltán (1959-) (fizikus) Beke Dezső László (1945-) (fizikus) Langer Gábor Antal (1950-) (fizikus) Greer, Lindsay A. Barber, Z. H. Kis-Varga Miklós
Internet cím:DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Rekordok letöltése1