001-es BibID:	BIBFORM085565
Első szerző:	Lexcellent, Christian
Cím:	High temperature creep measurements in equiatomic Ni-Ti shape memory alloy / C. Lexcellent, P. Robinet, J. Bernardini, D. L. Beke, P. Olier
Dátum:	2005
ISSN:	0933-5137
Megjegyzések:	High temperatures creep rates in equiatomic NiTi alloys at three different stress levels and at different temperatures have been measured. It was obtained that the creep rate can be well described by the Dorn equation with n=3. The activation energy of the effective diffusion coefficient, Dc (characterizing the Herring-Nabarro bulk creep) is Qc= 226 kJmole-1. From comparison of this value with the activation energy of Ni tracer diffusion (155 kJmol-1) it was concluded that the Ti is the slower component with high diffusion activation energy close to Qc. Hochtemperatur-Kriechraten in gleichatomigen NiTi-Legierungen wurden bei drei verschiedenen Spannungsniveaus und bei verschiedenen Temperaturen gemessen. Es hat sich gezeigt, dass die Kriechrate gut durch die Dorn-Gleichung mit n = 3 beschrieben werdenkann. DieAktivierungsenergiedeseffektiven Diffusionskoeffizienten Dc (charakteristisch fu?r das Herring-Nabarro-Kriechen) ist Qc= 226 kJmole-1. Durch Vergleich dieses Wertes mit der Aktivierungsenergie der Ni-Tracer-Diffusion (155 kJmol-1) konnte geschlossen warden, dass Ti die langsamere Komponente - mit einer Aktivierungsenergie nahe bei Qc - ist.
Tárgyszavak:	Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban folyóiratcikk creep shape memory alloy diffusion NiTi
Megjelenés:	Materialwissenschaft Und Werkstofftechnik. - 36 : 10 (2005), p. 509-512. -
További szerzők:	Robinet, P. Bernardini, Jean Beke Dezső László (1945-) (fizikus) Olier, P.
Pályázati támogatás:	T049513 OTKA
Internet cím:	Szerző által megadott URL DOI Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon: