Cím:	Fabrication of carbon fiber reinforced aluminum matrix composites via a titanium-ion containing flux / Baumli, P., Sychev, J., Budai, I., Szabo, J.T., Kaptay, G.
Dátum:	2013
ISSN:	1359-835X
Megjegyzések:	Here we show that carbon fiber (CF) reinforced aluminum (Al) matrix composite with homogenously 23dispersed (57 - 11 vol.%) carbon fibers can be fabricated without any external pressure, although usually 24some external pressure is needed to fabricate such composites due to their non-wetting character. CFs 25were transferred into liquid Al using a special flux (molten salt), containing K2TiF6 dissolved in 26NaCl-KCl. This flux ensures the removal of oxides from the interfaces and the formation of a wettable 27TiC layer at the interfaces. The oxide-free and in situ TiC-coated CF showed perfect wettability by the 28de-oxidized liquid Al under the same flux, and thus the composite was formed in a spontaneous way, 29i.e. without applying any external pressure or mixing.
Tárgyszavak:	Műszaki tudományok Anyagtudományok és technológiák idegen nyelvű folyóiratközlemény külföldi lapban Carbon fiber Metal matrix composites Wettability
Megjelenés:	Composites Part A-Applied Science And Manufacturing. - 44 (2013), p. 47-50. -
További szerzők:	Sychev, J. Szabo, J. T. Kaptay György Budai István (1977-) (folyamatmérnök)
Internet cím:	Szerző által megadott URL DOI Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon: