Találati lista | Tudóstér

001-es BibID:	BIBFORM060961
Első szerző:	Koleszár Péter (környezetkutató)
Cím:	Behaviour of ladle slag primary and secondary minerals in slag heap considering utilisation / Koleszár Péter, Papp István, Kozák Miklós, Kónya Péter, McIntosh Richard William, Grega Oszkár
Dátum:	2016
ISSN:	1842-4090 1844-489X
Megjegyzések:	Secondary steelmaking slags contain numerous types of minerals such as larnite and various Ca-aluminates. Fresh ladle slags are unstable in the atmosphere disintegrating into fine white dust. The modification change of larnite (C2S) is the main cause of this phenomenon. The freshly formed white slag powder is unprotected against wind erosion. When water is sprinkled on it, however, a solid crust is formed instantly. According to the results, this hard layer contains calcium aluminate hydrate causing quick bonding and reducing the threat of wind erosion significantly. The major composing minerals of slags belong to two groups: the gehlenite?akermanite series belonging to sorosilicates and the larnite?bredigite series that belong to nesosilicates. In very small quantities these slags also contain various heavy metals. The most characteristic among them is barium that is mostly precipitated as non-soluble barite in the course of the disintegration of the slag therefore it presence no environmental risk. The chemical composition of slags determines their possible utilization which is also discussed in the paper.
Tárgyszavak:	Természettudományok Földtudományok idegen nyelvű folyóiratközlemény külföldi lapban minimill ladle furnace deoxidisation oldhamite skarn minerals gehlenite tobermorite larnite OAM Ltd.
Megjelenés:	Carpathian Journal of Earth and Environmental Sciences. - 11 : 1 (2016), p. 17-26. -
További szerzők:	Papp István (1980-) (vegyész) Kozák Miklós (1948-) (geológus) Kónya Péter (1978-) (geográfus, geológia) McIntosh, Richard William (1978-) (geológus) Grega Oszkár (1948-) (villamosmérnök, okl. kohómérnök)
Internet cím:	Szerző által megadott URL Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon:

001-es BibID:	BIBFORM058585
Első szerző:	Koleszár Péter (környezetkutató)
Cím:	Behaviour of ladle slag minerals in atmospheric conditions regarding utilization / Koleszár Péter, Papp István, Miklós Kozák
Dátum:	2010
ISSN:	1788-4497
Megjegyzések:	The secondary steelmaking slags contain numerous minerals such as larnite, Ca-aluminates. The formed ladle slags areunstable in the atmosphere so they are dissociating to fine powder. The modification change of larnite (C2S) is the main cause of thisphenomenon. The fresh formed white slag powder is unprotected against wind erosion. The water sprinkling creates a solid layer on itinstantly. We have found that this layer contains calcium aluminate hydrate that causes rapid binding. This protective layer reduces theeffects of wind erosion significantly. Összefoglaló : A szekunder salakok sokféle ásványt tartalmaznak, amilyen például a larnit és a különféle kalcium- aluminátok. Aképződött salakok a levegőre kikerülve fehér porrá esnek szét, amit főként a larnit módosulása idéz elő. A frissen képződött fehér salakfokozottan szélerózió érzékeny. Vízzel történő locsolás hatására viszont szilárd kéreg képződik rajta. Vizsgálataink szerint ez a kötött rétegkalcium-aluminát-hidroxidokat tartalmaz, melyek a gyors kötés okozói. E védő burok hatására a szélerózió lehetősége jelentősen csökken.
Tárgyszavak:	Természettudományok Földtudományok idegen nyelvű folyóiratközlemény hazai lapban minimill Ladle Furnace oldhamite calcium-aluminate gehlenite
Megjelenés:	Acta geographica ac geologica et meteorologica Debrecina. Geology, Gemorphology, Physical Geography Series. - 4 : 5 (2010), p. 3-6. -
További szerzők:	Papp István (1980-) (vegyész) Kozák Miklós (1948-) (geológus)
Internet cím:	Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon:

001-es BibID:	BIBFORM058589
Első szerző:	Koleszár Péter (környezetkutató)
Cím:	Influence of slag minerals ont the utilisation of ladle slag / Koleszár Péter, Papp István
Dátum:	2011
Megjegyzések:	The scrap charge is melted down by the electric arc and oxyfuel jetburners such as in the Steelwork of Ózd Ltd. (OAM Ltd.). By the end of the heating the steel bath becomes oversaturated in oxygen. After casting gases would form eraised hollows as gas inclusions in the rolled steel products that are harmful. Other problems are the high inclusion and sulphur content. These parameters do not meet the requirements of the steel standards. These quality problems can be avoided by secondary refining. The standard technology consists of two technological steps. The first step is the precipitation deoxidation while the steel is under tapping. The next step is the diffusional deoxidation which is carried out in a ladle furnace where the steel obtains its final composition and the inclusions are floating into the slag and there they are absorbed. The arised slag called Ladle slag. This kind of slag contains skarn like Ca-silcate minerals such as: larnite, bredigite, gehlenite, mayenite and lime. After slag dumping these solid like slag at the slag pit tend to turn white fine dust, wich is exposed to wind erosion. It is prevented by water sprinking. The dissotiation of these slag is caused by the volume transformation of the larnite wich increased. By the sprinkling different secondary minerals are occour, wich forms solid bark on the surface of the slagpowder. These minerals are different calcium-silicate-hydrates(CSH) Calcium-aluminate-hydrates and Carbonates.We prove the presence of them. They determinate the behavior oft slag so we have to know their properties so we can optimize the recclyng tcchnology of them
ISBN:	978 963 661 955 8
Tárgyszavak:	Természettudományok Földtudományok előadáskivonat Ladle FurnaceLarnite OAM Ltd. volume stability deoxidation calcite spurrite
Megjelenés:	XXV. microCAD : International Scientific Conference - Earth science and engineering / ed. Bikfalvi Péter. - p. 1-5. -
További szerzők:	Papp István (1980-) (vegyész)
Internet cím:	Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon:

001-es BibID:	BIBFORM058586
Első szerző:	Papp István (vegyész)
Cím:	Chemical composition and zinc leaching test of dust from electric arc furnace emissions from the Steelwork of Ózd, Hungary / Papp István, Koleszár Péter, Miklós Kozák
Dátum:	2010
ISSN:	1788-4497
Megjegyzések:	The recycling of metallurgical by-products is vital for both economical or environmental reasons. Electric arc furnace dusts areconsidered as secondary raw materials for zinc production. In this paper we investigated the chemical composition of the EAF dusts ofthe Steelwork of Ózd, Hungary. The total zinc content of the EAF dust is 24-25 (m/m)%, and 16-17 (m/m)% is leachable with anammonium carbonate solution. The EAF dust of Ózd Steelwork should be considered as a potential raw material for hydrometallurgicalZn production.Összefoglalás ? A fémipari hulladékok újrahasznosítása környezetvédelmi és gazdaságossági szempontból is lényeges. Az acélgyártássorán a füstgázokból leválasztott porok másodlagos nyersanyagokként elsősorban a cinktermelésben jöhetnek szóba. Jelen cikkünkben azÓzdi Acélművek ívkemencéjének füstgázaiból leválasztott por kémiai összetételét vizsgáltuk. A leválasztott por cinktartalma átlagosan 24-25 (m/m)%, melyből 16-17 (m/m)%-nyi mennyiség kioldható ammónium-karbonáttal. Véleményünk szerint a füstgázból leválasztott porhidrometallurgiai módszerekkel újrahasznosítható másodlagos nyersanyag.
Tárgyszavak:	Természettudományok Földtudományok idegen nyelvű folyóiratközlemény hazai lapban steel production furnace dust secondary raw material Ózd
Megjelenés:	Acta geographica ac geologica et meteorologica Debrecina. Geology, Gemorphology, Physical Geography Series. - 4 : 5 (2010), p. 7-11. -
További szerzők:	Koleszár Péter (1981-) (környezetkutató) Kozák Miklós (1948-) (geológus)
Internet cím:	Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon: