1.

001-es BibID:BIBFORM118616
035-os BibID:(cikkazonosító)113699 (WoS)001179768800001 (Scopus)85183974343
Első szerző:Gulyás Szilvia (fizikus)
Cím:The effect of self-organization during deposition on the segregation behaviour of Au in the Si-Ge-Au nano-multilayer thermoelectric generator system / Szilvia Gulyás, Gábor L. Katona, Gábor Csiszár, János J. Tomán, Csaba Cserháti, Zoltán Erdélyi
Dátum:2024
ISSN:1044-5803
Megjegyzések:Si-Ge-Au amorphous-nanocrystalline composites are important thermoelectric materials where the Seebeck coefficient and the electrical conductivity may be tuned independently. There are many attempts to improve the thermoelectric properties of Si/Ge systems by the addition of additives like Au. However, the effectiveness of doping and the role of Au is not clear. We report on structural transformations and Au segregation behaviour in post-annealed sputter deposited multilayer thin films using composition depth profiling, electron microscopy, xray diffraction and computer simulation. We show that depending on the nominal thickness of the initial Au layers the film volume becomes depleted of Au for thinner Au layers while for thicker Au layers the Au content is much higher in the form of large precipitates. Due to the self-organization and changing of microstructure during deposition the segregation of Au is very different for different Au individual layer thicknesses. In case of thinner Au layers it is enriched at the free surface, while for thicker initial Au layer thickness gold accumulated at the substrate. We have carried out computer simulations based on stochastic kinetic mean-field model. These calculations support the argument that initial Au island size can drastically affect the dissolution/growth and segregation behaviour of gold which can significantly influence the thermoelectric parameters. Based on these results we provide a possible explanation to the difference in thermoelectric properties found in the literature.
Tárgyszavak:Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban
folyóiratcikk
thermoelectric sigeau
nucleation and growth
multilayer thin film
experiments and computer simulations
microstructure dependent segregation of au
au doping
Megjelenés:Materials Characterization. - 209 (2024), p. 113699-. -
További szerzők:Katona Gábor (1977-) (fizikus) Csiszár Gábor (fizikus) Tomán János (1987-) (fizikus) Cserháti Csaba (1963-) (fizikus) Erdélyi Zoltán (1974-) (fizikus)
Pályázati támogatás:TKP2021-NKTA-34
Egyéb
TKP2021-NKTA
Egyéb
2019-2.1.11-TÉT-2019-00061
Egyéb
Internet cím:Szerző által megadott URL
DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító:

2.

001-es BibID:BIBFORM086707
035-os BibID:(cikkazonosító)365404
Első szerző:Kruhlov, Ivan O.
Cím:Structural phase transformations in annealed Pt/Mn/Fe trilayers / I. O. Kruhlov, O. V. Shamis, N. Y. Schmidt, M. V. Karpets, S. Gulyas, E. Hadjixenophontos, A. P. Burmak, S. I. Sidorenko, G. L. Katona, G. Schmitz, M. Albrecht, I. A. Vladymyrskyi
Dátum:2020
ISSN:0953-8984 1361-648X
Tárgyszavak:Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban
folyóiratcikk
chemical ordering
solid state reactions
magnetic thin films
Ll0-mnpt
Megjelenés:Journal Of Physics-Condensed Matter. - 32 : 36 (2020), p. 1-9. -
További szerzők:Shamis, O. V. (fizikus) Schmidt, N. Y. Karpets, M. V. Gulyás Szilvia (1993-) (fizikus) Hadjixenophontos, E. Burmak, A. P. Sidorenko, Sergey I. Katona Gábor (1977-) (fizikus) Schmitz, Guido Albrecht, Manfred Vladymyrskyi, Igor A.
Pályázati támogatás:GINOP-2.3.2-15-2016-00041
GINOP
Internet cím:Szerző által megadott URL
DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító:

3.

001-es BibID:BIBFORM086609
035-os BibID:(cikkazonosító)138134
Első szerző:Kruhlov, Ivan O.
Cím:Thermally-induced phase transitions in Pt/Tb/Fe trilayers / I. O. Kruhlov, O. V. Shamis, N. Y. Schmidt, S. Gulyas, R. Lawitzki, A. P. Burmak, S. I. Konorev, G. L. Katona, G. Schmitz, M. Albrecht, I. A. Vladymyrskyi
Dátum:2020
ISSN:0040-6090
Tárgyszavak:Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban
folyóiratcikk
diffusion intermixing
solid state reactions
magnetic thin films
terbium
l10-ordered iron-platínum
Megjelenés:Thin Solid Films. - 709 (2020), p. 1-7. -
További szerzők:Shamis, O. V. (fizikus) Schmidt, N. Y. Gulyás Szilvia (1993-) (fizikus) Lawitzki, R. Burmak, A. P. Konorev, S. I. Katona Gábor (1977-) (fizikus) Schmitz, Guido Albrecht, Manfred Vladymyrskyi, Igor A.
Pályázati támogatás:GINOP-2.3.2-15-2016-00041
GINOP
Internet cím:Szerző által megadott URL
DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító:

4.

001-es BibID:BIBFORM103238
035-os BibID:(WOS)000570817200001 (Scopus)85091078768
Első szerző:Makushko, P. V.
Cím:Formation of ordered L10-FePt phase in FePt-Ag thin films / P. V. Makushko, M. N. Shamis, N. Y. Schmidt, I. E. Kotenko, S. Gulyas, G. L. Katona, T. I. Verbytska, D. L. Beke, M. Albrecht, Iu M. Makogon
Dátum:2020
ISSN:2190-5509 2190-5517
Megjegyzések:In this work, the influence of an Ag layer, which is located at different positions of the layer stack (top, intermediate, bottom), on the structural and magnetic properties of orderedL1(0)phase in Fe(50)Pt(50)films was investigated. It was found that the position of an additional Ag layer affects the stress state of the as-deposited FePt films. Mechanical stress is induced during deposition and post-annealing process due to the difference in thermal expansion coefficients and lattice mismatch of FePt, Ag, and substrate. The initial stress state affects the ordering process during subsequent heat treatment. The higher level of initial compressive stress (- 7.8 GPa) in FePt/Ag/FePt films results inL1(0)phase formation at a temperature of 700 degrees C which is about 100 degrees C lower than in films with Ag bottom (- 3.6 GPa) and top (+ 0.86 GPa) layers. A more pronounced (001) oriented growth of theL1(0)phase was observed in stacks with Ag top layer as compared to Ag bottom and intermediate layers. The highest values of coercivity were obtained for films with Ag intermediate and bottom layers, which is due to the distribution of Ag along FePt grain boundaries that result in strong exchange decoupling of FePt grains. Furthermore, the formation of the orderedL1(0)phase at comparatively low temperatures of about 370 degrees C was observed in a free-standing FePt/Ag (30 nm)/FePt film.
Tárgyszavak:Természettudományok Fizikai tudományok konferenciacikk
folyóiratcikk
Stress state
Annealing
Ordering
L1(0)-FePt phase
Coercivity
Megjelenés:Applied Nanoscience. - 10 : 12 (2020), p. 4809-4816. -
További szerzők:Shamis, M. N. Schmidt, N. Y. Kotenko, I. E. Gulyás Szilvia (1993-) (fizikus) Katona Gábor (1977-) (fizikus) Verbytska, T. I. Beke Dezső László (1945-) (fizikus) Albrecht, Manfred Makogon, I. M.
Pályázati támogatás:V4EaP Scholar-ship 51300654
Egyéb
GINOP-2.3.2-15-2016-00041
GINOP
Internet cím:Szerző által megadott URL
DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító:

5.

001-es BibID:BIBFORM079100
Első szerző:Shamis, O. V. (fizikus)
Cím:Phase transformations in Pt/Fe bilayers during post annealing probed by resistometry / O. V. Shamis, N. Y. Safonova, M. M. Voron, A. P. Burmak, S. I. Sidorenko, G. L. Katona, S. Gulyas, D. L. Beke, M. Albrecht, I. A. Vladymyrskyi
Dátum:2019
ISSN:0953-8984 1361-648X
Megjegyzések: X-ray diffraction (XRD), secondary neutral mass spectrometry (SNMS) depth profiling, and electrical resistivity measurements were used to follow the phase transformations in Pt/Fe bi-layered thin films during annealing. Initially, the electrical resistivity increases linearly with temperature up to 150 °C due to the contribution of phonon scattering of the metallic Pt and Fe bilayer. Further increase of the annealing temperature leads to a steeper linear increase, which is associated with the initial formation of the chemically disordered A1-phase followed by the formation of the chemically ordered L10-FePt phase, as confirmed by XRD and SNMS studies. Finally, at about 620 °C the single L10-FePt phase has formed throughout the film. Moreover, the electrical resistivity contains also the magnetic contribution to the total resistivity. In this case, the loss in magnetic order is indicated by a change in temperature dependence of the resistivity at about 310 °C, representing the Curie temperature of the initially formed A1-FePt alloy, while the finally formed L10-FePt alloy reveals a higher magnetic transition temperature of about 410 °C. In this study, it has been demonstrated that resistometry in combination with structural and chemical analysis provides valuable information on diffusion processes, structural phase formations and its stability range, as well as on the magnetic transition temperature.
Tárgyszavak:Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban
electrical resistivity
chemical ordering
magnetic thin films
FePt
Megjelenés:Journal Of Physics-Condensed Matter. - 31 : 28 (2019), p. 285401-. -
További szerzők:Safonova, N. Y. Voron, M. M. Burmak, A. P. Sidorenko, Sergey I. Katona Gábor (1977-) (fizikus) Gulyás Szilvia (1993-) (fizikus) Beke Dezső László (1945-) (fizikus) Albrecht, Manfred Vladymyrskyi, Igor A.
Pályázati támogatás:GINOP-2.3.2-15-2016-00041
GINOP
Internet cím:Szerző által megadott URL
DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító: