001-es BibID:	BIBFORM002192
Első szerző:	Carmona, Humberto A.
Cím:	Computer simulation of fatigue under diametrical compression / H. A. Carmona, F. Kun, J. S. Andrade Jr., H. J. Herrmann
Dátum:	2007
ISSN:	2470-0045 2470-0053
Megjegyzések:	We study the fatigue fracture of disordered materials by means of computer simulations of a discrete element model. We extend a two-dimensional fracture model to capture the microscopic mechanisms relevant for fatigue, and we simulate the diametric compression of a disc shape specimen under a constant external force. The model allows to follow the development of the fracture process on the macro- and micro-level varying the relative influence of the mechanisms of damage accumulation over the load history and healing of microcracks. As a specific example we consider recent experimental results on the fatigue fracture of asphalt. Our numerical simulations show that for intermediate applied loads the life time of the specimen presents a power law behavior. Under the effect of healing, more prominent for small loads compared to the tensile strength of the material, the life time of the sample increases and a fatigue limit emerges below which no macroscopic failure occurs. The numerical results are in a good qualitative agreement with the experimental findings.
Tárgyszavak:	Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban fracture fatigue discrete element model computer simulation
Megjelenés:	Physical Review E. - 75 : 4 (2007), 046115. -
További szerzők:	Andrade, J. S. Herrmann, Hans J. Kun Ferenc (1966-) (fizikus)
Internet cím:	Intézményi repozitóriumban (DEA) tárolt változat Szerző által megadott URL DOI
Borító:
Saját polcon:

001-es BibID:	BIBFORM002190
Első szerző:	Kun Ferenc (fizikus)
Cím:	Fatigue failure of disordered materials [elektronikus dokumentum] / F. Kun; M. H. Costa; R. N. Costa Filho; J. S. Andrade; J. B. Soares; S. Zapperi; H. J. Herrmann
Dátum:	2007
Megjegyzések:	We present an experimental and theoretical study of the fatigue failure of heterogeneous materials under cyclic compression considering asphalt as a specific example. Varying the load amplitude, experiments reveal a finite fatigue limit below which the specimen does not break, while approaching the tensile strength of the material a rapid failure occurs. In the intermediate load range, the lifetime decreases with the load as a power law. We introduce two novel theoretical approaches, namely, a fiber bundle model and a fuse model, and show that both capture the major microscopic mechanisms of the fatigue failure of heterogeneous materials, providing an excellent agreement with the experimental findings. Hozzáférés: World Wide Web
Tárgyszavak:	Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban fracture fatigue fiber bundle
Megjelenés:	Journal of Statistical Mechanics [elektronikus dokumentum] : Theory and experiment. - 7 (2007), p. 02003. -
További szerzők:	Costa, M. H. Costa Filho, R. N. Andrade, J. S. Soares, J. B. Zapperi, S. Herrmann, Hans J.
Internet cím:	elektronikus változat