Magyar
Toggle navigation
Tudóstér
Magyar
Tudóstér
Keresés
Egyszerű keresés
Összetett keresés
CCL keresés
Egyszerű keresés
Összetett keresés
CCL keresés
Böngészés
Saját polc tartalma
(
0
)
Korábbi keresések
CCL parancs
CCL
Összesen 2 találat.
#/oldal:
12
36
60
120
Rövid
Hosszú
MARC
Részletezés:
Rendezés:
Szerző növekvő
Szerző csökkenő
Cím növekvő
Cím csökkenő
Dátum növekvő
Dátum csökkenő
1.
001-es BibID:
BIBFORM043728
Első szerző:
Szalóki Melinda (vegyész)
Cím:
Preparation of reactive polymeric nanoparticles / Melinda Szaloki, Robert Scribanek, John F. Hartmann, Csaba Hegedus, Janos Borbely
Dátum:
2006
Megjegyzések:
Polyreactions of multivinyl monomers in emulsion droplets lead to formation of crosslinked macromolecules. In the emulsion polymerization the surfactant-mediated nanoparticles involves the monomers serving as nanoreactors. It prevents gelation while allowing the growth of particles the defined volume. In this study we describe the formation of reactive polymeric nanoparticles (RPNPs) for potential use as dental materials or as a component of industrial powder coatings. As dental filling materials, since the predominant portion of polymerization is performed in advance, limited volumetric shrinking is expected to be observed during the final in situ photopolymerization step. On the other hand no necessary or limited use of toxic monomers is required. The correlation of monomer feed, crosslinking density, particle size, reactivity and swelling behavior of RPNPs is described.
Tárgyszavak:
Természettudományok
Kémiai tudományok
konferenciacikk
Polymeric nanoparticles
Megjelenés:
Polymeric Materials : Science & Engineering. - 94 : 1 (2006), p. 783-784. -
További szerzők:
Skribanek Róbert
Hartmann, John F.
Hegedűs Csaba (1953-) (fogszakorvos)
Borbély János (1950-) (vegyész)
Internet cím:
Szerző által megadott URL
Intézményi repozitóriumban (DEA) tárolt változat
Szerző által megadott URL
Borító:
Saját polcon:
2.
001-es BibID:
BIBFORM006969
Első szerző:
Szalóki Melinda (vegyész)
Cím:
Preparation of reactive polymeric nanoparticles (RPNPs) / Melinda Szaloki, Robert Skribanek, Zsolt Dudas, John F. Hartmann, Csaba Hegedűs, Janos Borbely
Dátum:
2008
Megjegyzések:
A series of reactive polymeric nanoparticles (RPNPs) was prepared by free radical nonlinear copolymerization of mono (M 1) and trivinyl acrylic (M 2) monomers in miniemulsion. The crosslinking density was determined by the mole ratio of the trivinyl component. It was found that the unswelled latex nanoparticles showed a narrower dispersity than in the organic solution of macromolecules. In latex, the size increased with the ratio of M 2 monomer due to its higher polarity in the aqueous medium. However, the swollen nanoparticles, dissolved or dispersed in organic solvent, showed a higher dispersity as a function of composition and the crosslinking density. The residual vinyl groups adjacent to the nanoparticles were subjected to further crosslinking reactions. The reactive vinyl groups were detected by nuclear magnetic resonance spectroscopy (NMR). The size of particles in swollen state was determined by dynamic laser light scattering (DLS) method and the dried form by scanning electron microscopy (SEM). It was found that size of RPNPs is in the range of 50 to 500 nm. These particles possess properties that may allow their application in areas as disparate as dental filling material and as a component in industrial powder-based coatings.
Tárgyszavak:
Orvostudományok
Klinikai orvostudományok
idegen nyelvű folyóiratközlemény külföldi lapban
Free radical nonlinear polymerization
Reactive Polymeric Nanoparticles (RPNPs)
Miniemulsion
Number average vinyl functionality (NAVF)
Crosslinking polymerization
Megjelenés:
Colloid and Polymer Science. - 286 : 4 (2008), p. 435-444. -
További szerzők:
Skribanek Róbert
Dudás Zsolt
Hartmann, John F.
Hegedűs Csaba (1953-) (fogszakorvos)
Borbély János (1950-) (vegyész)
Internet cím:
elektronikus változat
DOI
Szerző által megadott URL
Borító:
Saját polcon:
Rekordok letöltése
1
Corvina könyvtári katalógus v8.2.27
© 2023
Monguz kft.
Minden jog fenntartva.