Cím:Synthesis of biogenic calcium silicate glasses from biomass : Physical, dielectric and electrical properties / Sharma Gaurav, Sharma Deepanshu, Singh Kuljeet, Jha Praveen, Bansal Neetu, Mishra Yogendra K., Singh K., Sharma Abhishek, Sharma Sanjeev K.
Dátum:2023
ISSN:0022-3093
Megjegyzések:Biogenic calcium silicate glasses were synthesized from the biomass wastes by melt-quench technique at a high temperature of 1550 ?C. XRD pattern showed the preferred orientation along the c-axis (002) regardless of the concentration of eggshell powder. The optical bandgap (Eg) decreased from 3.96 to 3.74 eV, and the refractive index (n) increased from 2.17 to 2.22 as ESP risen from 0 to 25 wt.%. The dielectric constant (?· ) of sintered glasses was measured at 1 kHz and 1 MHz to be 40?135 and 27?44, respectively. The decreasing, ?· and tan? with respect to concerning temperature is attributed to the most miniature hopping mechanism. The ?ac of SE-3(H) was observed to be the lowest (5.26 ? 10? 7 S/m) at 400 ?C due to the lower volume of non-bridging oxygen. The study of silicate glasses suggests the major applications in the semiconductor industries, the sealing of energy harvesting and energy storage devices.
Tárgyszavak:Természettudományok Kémiai tudományok idegen nyelvű folyóiratközlemény külföldi lapban
folyóiratcikk
Megjelenés:Journal Of Non-Crystalline Solids. - 612 (2023), p. 1-8. -
További szerzők:Sharma, Deepanshu Singh, Kuljeet (1988-) (biokémia, sejtbiológia, molekuláris biológia) Jha, Praveen Bansal, Neetu Mishra, Yogendra K. Singh, Kulwant Sharma, Abhishek Sharma, Sanjeev K.
Internet cím:Szerző által megadott URL
DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Rekordok letöltése1 
Corvina könyvtári katalógus v8.2.27 © 2023 Monguz kft. Minden jog fenntartva.