Első szerző:	Gaál Zoltán Tamás (fizikus)
Cím:	Boron depth distribution in iron surfaces at high-dose implantation / Z. T. Gaál, Z. Halász, A. Csík, V. Takáts, G. Nagy, J. Oscarsson, M. Sortica, D. Primetzhofer, T. Fodor, S. Molnár, J. Hakl, Zs. Benkó, L. Daróczi, M. Benke, K. Vad, I. Rajta
Dátum:	2025
ISSN:	0042-207X
Megjegyzések:	Due to application of lead-free materials in soldering technology, the degradation of industrial tools is accelerated. However, this can be circumvented with boriding. Two types of boride phases are usually formed (FeB and Fe2B), causing internal stress due to the different crystal structures. Our aim with B+ ion implantations is to avoid this weakness and create a single-phase iron boride layer. The ion implantation was performed at different doses (6.9.1017-1.1018 ions/cm2) of boron ions and with bombarding energies of 25 keV and 100 keV. The depth distribution of implanted boron was investigated by Secondary Neutral Mass Spectrometry (SNMS) depth profile analyses, Scanning Electron Microscopy (SEM) measurements, and by Elastic Recoil Detection Analysis (ERDA). The purpose of these measurements was to obtain information about the boron distribution produced by high-dose implantation. Our experimental analyses show that the boron distribution is more of a Pearson IV type than a Gaussian type.
Tárgyszavak:	Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban folyóiratcikk nagy dózis implantálás
Megjelenés:	Vacuum. - 238 (2025), p. 1-6. -
További szerzők:	Halász Zoltán (1975-) (fizikus) Csik Attila (1975-) (fizikus) Takáts Viktor Nagy Gyula (1986-) (környezetkutató fizikus) Oscarsson, Johan Sortica, Mauricio Primetzhofer, Daniel Fodor Tamás (1984-) (Ph.D hallgató) Molnár Sándor (1990-) (fizikus) Hakl József Benkó Zsolt (1980-) (geológus) Daróczi Lajos (1965-) (fizikus) Benke Márton Vad Kálmán Rajta István (1970-) (fizikus)
Pályázati támogatás:	RADIATE project Grant Agreement No. 824096 Egyéb TKP2021-NKTA-42 Egyéb
Internet cím:	Szerző által megadott URL DOI Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon:

001-es BibID:	BIBFORM086135
Első szerző:	Molnár Sándor (fizikus)
Cím:	Kinetics of photo-darkening and -bleaching in amorphous As20Se80 layers : temperature dependence / S. Molnar, R. Bohdan, V. Takats, Yu. Kaganovskii, K. Vad, S. Kokenyesi
Dátum:	2018
ISSN:	1454-4164 1841-7132
Megjegyzések:	Photo-darkening (PD) and surface relief (SR) recording is applicable for fabrication of photonic elements in amorphous chalcogenides. While SR in As20Se80 layers was found very efficient, the influence of PD on recording and thermal stability need to be established. Thermally activated transient and reversible components of PD were detected. From temperature dependent characteristic times of recording and erasing for both PD components rather low activation energies (17 and 13 meV) for the recording process and high activation energies (210 and 90 meV) for erasing were determined. The mechanisms of relevant processes and stability of optical relief recording are discussed.
Tárgyszavak:	Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban folyóiratcikk
Megjelenés:	Journal of Optoelectronics and Advanced Materials. - 20 : 11-12 (2018), p. 646-650. -
További szerzők:	Bohdan, Roland Takáts Viktor Kaganovskii, Yuri S. Vad Kálmán Kökényesi Sándor (1946-) (fizikus)
Pályázati támogatás:	GINOP-2.3.2-15-2016-00041 GINOP
Internet cím:	Intézményi repozitóriumban (DEA) tárolt változat