Cím:Evaluation of the Effect of the Microscopic Glass Surface Protonation on the Hard Tissue Thin Section Preparation / Szalóki Melinda, Hegedűs Viktória, Fodor Tamás, Martos Renáta, Radics Tünde, Hegedűs Csaba, Dezső Balázs
Dátum:2020
ISSN:2076-3417
Megjegyzések:In this study, a new procedure for mounting tissue blocks was described while cutting and grinding the section remains tightly bound to the inert glass surface both chemically and micro mechanically allowing good quality specimens for staining and microscopic analysis. The micromechanical interlocking was achieved by using of frosted glass, the chemical binding was made with 10-methacryloyloxydecyl dihydrogen phosphate monomer (10-MDP) containing bond material. The glass surface activation was achieved by nitric acid etching and the surface was characterized by zeta potential, X-ray photoelectron spectroscopy (XPS), and contact angle measurements. Cylindrical samples were prepared from epoxy embedding materials, cortical bovine bone, and dental titanium to investigate the shear bond strengths (SBS) to microscopic glass slide compared to a routinely used thermoplastic adhesive. Based on the experiments it was found that the micromechanical retention combined with MDP containing bond material improved the SBS data compared to the thermoplastic adhesive. The acid etched glass became positively charged that significantly increased the SBS data of bone and titanium compared with the uncharged version. Therefore, the thickness of the undecalcified bone section with metal can safely reduce to improve histological microscopic analysis.
Tárgyszavak:Orvostudományok Klinikai orvostudományok idegen nyelvű folyóiratközlemény külföldi lapban
folyóiratcikk
microscopic glass surface protonation
nitric acid etching
undecalcified thin bone section
titanium implant
10-MDP
adhesion
Megjelenés:Applied Sciences-Basel. - 10 : 21 (2020), p. 1-21. -
További szerzők:Hegedűs Viktória (1986-) (fogorvos) Fodor Tamás (1984-) (Ph.D hallgató) Martos Renáta (1975-) (fogszakorvos) Radics Tünde (1963-) (egyetemi adjunktus, fogszakorvos) Hegedűs Csaba (1953-) (fogszakorvos) Dezső Balázs (1951-) (pathológus)
Pályázati támogatás:GINOP-2.3.2.-15-2016-00011
GINOP
GINOP-2.3.2.-15-2016-00022
GINOP
GINOP-2.3.2.-15-2016-00041
GINOP
Internet cím:Szerző által megadott URL
DOI
Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Rekordok letöltése1