Cím:	Surface patterning in Ge-Se amorphous layers / I. Csarnovics, M. Veres, P. Nemec, M. R. Latif, P. Hawlova, S. Molnar, S. Kokenyesi
Dátum:	2017
ISSN:	0022-3093
Megjegyzések:	Compositional and fabrication method dependences of laser-induced geometrical surface relief formation in Ge-Se amorphous layers were investigated with the aim to determine the possible role of initial conditions in the mechanism and efficiency of optical recording. The results show that pulsed laser deposition has some advantages in composition preservation and surface relief formation in comparison with thermal evaporation for producing layers with high sensitivity and efficiency of surface relief grating formation, especially in layers with Ge24Se76 composition. It was shown that modulation depth of the created surface structures increases with increasing Se content in Ge-Se amorphous chalcogenide layers. Thermal annealing has essential influence on the recording parameters, enabling additional insight into the possible mechanisms of light induced surface patterning in this type of light-sensitive amorphous chalcogenides. Raman spectroscopy was used to identify local structure of produced surface patterns.
Tárgyszavak:	Természettudományok Fizikai tudományok idegen nyelvű folyóiratközlemény külföldi lapban folyóiratcikk amorphous chalcogenides Ge-Se system thin films light induced surface pattering raman spectroscopy atomic force microscopy
Megjelenés:	Journal of Non-Crystalline Solids. - 459 (2017), p. 51-56. -
További szerzők:	Veres Miklós Nemec, Petr Latif, Muhamma Rizwa Hawlova, P. Molnár Sándor (1990-) (fizikus) Kökényesi Sándor (1946-) (fizikus)
Pályázati támogatás:	TÁMOP4.2.4.A/2-11-1-2012-0001 TÁMOP TÁMOP-4.2.2.A-11/1/KONV-2012-0036 TÁMOP
Internet cím:	Szerző által megadott URL DOI Intézményi repozitóriumban (DEA) tárolt változat
Borító:
Saját polcon: